3M™ Dyneon™ PTFE TF 1750
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLqQZP_3M-Dyneon-PTFE-TF-1750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Non free-flowing PTFE for compression moulding Features
Typical applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.16 | g/cm³ | ISO 12086 |
| Apparent Density | 0.38 | g/cm³ | ISO 60 |
| Molding Shrinkage | 4.3 | % | Internal Method |
| Average Particle Size | 25 | µm | ISO 13320 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 600 | MPa | ISO 527-2 |
| Deformation Under Load | ASTM D621 | ||
| 15 MPa 1 | 10.0 | % | |
| 15 MPa 2 | 17.0 | % | |
| 15 MPa 3 | 16.0 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (100 µm) | 42.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 100 µm) | 430 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | DIN 53752 | ||
| 30 to 100°C | 1.2E-4 | cm/cm/°C | |
| 30 to 200°C | 1.4E-4 | cm/cm/°C | |
| 30 to 260°C | 1.7E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength (0.100 mm) | 88 | kV/mm | ISO 12086 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | permanent |
| 2 . | 100 hr |
| 3 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 3084H | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| 4PROP® 9C22440 | 4Plas | PP Copolymer | 4PROP® |
| Fluon® PFA P-65PT | Asahi Glass Co., Ltd. | PFA | Fluon® |
| Hypro-G™ PP-HP4 | Entec Polymers | PP Homopolymer | Hypro-G™ |
| Durethan® BKV 115 DUS008 000000 | LANXESS Corporation | Nylon 6 | Durethan® |