Karina IVORY PVC COMPOUND 105902-35/ 1-Y-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLDznm_Karina-IVORY-PVC-COMPOUND-105902-35-1-Y-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND RECOMMENDED FOR THIN WALL INSULATION OF AUTOMOTIVE ELECTRICAL WIRES FOR WORKING AT THE TEMPERATURE RANGE OF - 40C TO 105C. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.29 to 1.35 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -2.38 to 1.22 | ME 12 | |
| Color b | 6.29 to 9.89 | ME 12 | |
| Color L | 87.7 to 91.3 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 44 to 48 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VE50C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| GLAMIDE® T-403 | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| EMERGE™ PC 4350 | Trinseo | PC | EMERGE™ |
| LNP™ THERMOCOMP™ RF006XXJ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| TABOREN® PH 22 B 25 | SILON s.r.o. | PP Homopolymer | TABOREN® |