| Medium Viscosity Acetal Homopolymer with Improved Processing |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 2.0 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 1.4 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 92 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 71.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 17 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2800 | MPa | |
| 1000 hr | 1600 | MPa | |
| Flexural Modulus | 2950 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 280 | kJ/m² | |
| 23°C | 320 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 250 | kJ/m² | |
| 23°C | 280 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 3.00 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 2000 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/B50 |
| Ball Pressure Test (165°C) | Pass | IEC 60309-1 | |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 44 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-3 | ||
| 1 MHz | 5.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 22 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 8.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 30 GREEN | SRF Ltd. | Nylon 6 | TUFNYL® |
| Vyncolit® RX®3-1-501N-P | Vyncolit N.V. | DAP | Vyncolit® |
| ExxonMobil™ LLDPE LL 5252.09 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Gazprom PSM-115N (Prime Grade) | JSC Gazprom neftekhim Salavat | PS (GPPS) | Gazprom |
| Karina RED PVC COMPOUND 800D42/332-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |