Envir® PA66G15VHL-BK0704
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Barnet |
| Trademark: | Envir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cHMmDG_Envir-PA66G15VHL-BK0704.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Envir® PA66G15VHL-BK0704 is a 15% Glass fiber reinforced Nylon 66 molding resin that is also Toughened. 66G15VHL offers a good balance of properties and excellent processibility. It is a value added "upcycled" resin with a truly "green" appeal. It is provided Black in color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 20.0 | cm³/10min | ASTM D1238 |
| Ash Content | 15 | % | ASTM D5630 |
| Moisture Content | < 0.20 | % | ASTM D6980 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Granularity | 3.40 | g/100 pellets |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 95.0 | MPa | |
| Break | 93.0 | MPa | |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 4900 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Spartech Polycom SC7F-7010R | Spartech Polycom | PC | Spartech |
| WanBlend® WHT-HF9485K2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| TROSIFOL® HR100 | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| Durethan® BKV 30 G H2.0 900051 | LANXESS Corporation | Nylon 6 | Durethan® |