Generic PSU - Glass Fiber
| Category: | PSU , Polysulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cGGIGT_Generic-PSU---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PSU - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 - 1.62 | g/cm³ | ASTM D792 |
| 23°C | 1.38 - 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.42 | % | ASTM D955 |
| 23°C | 0.22 - 0.85 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 121 - 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3030 - 10400 | MPa | ASTM D638 |
| 23°C | 8350 - 9400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 68.9 - 124 | MPa | ASTM D638 |
| Fracture, 23°C | 72.4 - 140 | MPa | ASTM D638 |
| Fracture, 23°C | 87.0 - 135 | MPa | ISO 527-2 |
| 23°C | 75.2 - 108 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.3 - 5.1 | % | ASTM D638 |
| Fracture, 23°C | 1.2 - 7.1 | % | ASTM D638 |
| Fracture, 23°C | 1.3 - 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3280 - 9890 | MPa | ASTM D790 |
| 23°C | 6000 - 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 109 - 159 | MPa | ASTM D790 |
| 23°C | 120 - 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 52 - 82 | J/m | ASTM D256 |
| 23°C | 5.9 - 8.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 370 - 590 | J/m | ASTM D256 |
| 23°C | 24 - 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 182 - 188 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 180 - 186 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 173 - 186 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 174 - 185 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| -- | 3.0E-5 - 3.2E-5 | cm/cm/°C | ASTM D696 |
| -- | 1.7E-5 - 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+3 - 1.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 17 - 19 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.15 - 3.75 | ASTM D150 | |
| Dissipation Factor (23°C) | 7.0E-4 - 6.2E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 137 | °C | |
| Drying Time | 3.5 - 4.0 | hr | |
| Suggested Max Moisture | 0.049 - 0.050 | % | |
| Rear Temperature | 330 - 338 | °C | |
| Middle Temperature | 336 - 343 | °C | |
| Front Temperature | 334 - 354 | °C | |
| Processing (Melt) Temp | 351 - 367 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Injection Pressure | 95.3 - 98.1 | MPa | |
| Back Pressure | 0.258 - 0.517 | MPa | |
| Screw Speed | 45 - 55 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PSU - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GAPEX® RPP20EB09UL NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Keltan® 9950 | LANXESS Buna GmbH | EPDM | Keltan® |
| Jamplast JPEVA18 | Jamplast, Inc. | EVA | Jamplast |
| KEBAFORM® C 270 LS black | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Crastin® SK605LM BK591 | DuPont Performance Polymers | PBT | Crastin® |