LNP™ LUBRICOMP™ EX06405 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cFuIid_LNPLUBRICOMPEX06405compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. Also known as: LNP* LUBRICOMP* Compound EFL-4034 EM LE Product reorder name: EX06405 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.53 | g/cm³ | ASTM D792 |
| -- | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.42 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- | 7140 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 123 | MPa | ASTM D638 |
| Yield | 119 | MPa | ISO 527-2 |
| Fracture | 123 | MPa | ASTM D638 |
| Fracture | 119 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.4 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2 |
| Fracture | 2.4 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 6900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 152 | MPa | ASTM D790 |
| -- | 169 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.44 | ASTM D3702 Modified | |
| With Self-Static | 0.52 | ASTM D3702 Modified | |
| Wear Factor - Washer | 69.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.8 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 209 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 211 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 202 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 204 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC A50-EG | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| DURACON® GH-10 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| HiFill® PA6/6 GF33 LE | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| ESTOPLAST EP 4140GY11 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| tivilon® M 70 Dx 1 | API SpA | TPV | tivilon® |