XANTAR® C CM 526
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cFgE7Y_XANTARCCM526.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.40 | % | ISO 294-4 |
| Flow | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 45.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/4A | ||
| -20°C | 14 | kJ/m² | ISO 180/4A |
| 23°C | 25 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 131 | °C | ISO 306/B50 |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.00 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.5 mm) | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (3.0 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecodur® PB30 NL | Eurotec Engineering Plastics | PBT | Tecodur® |
| Thermoset Plastics 285 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| TIPPLEN® H 681 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| LNP™ THERMOCOMP™ JF003E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| Petrothene® GA501154 | LyondellBasell Industries | LLDPE | Petrothene® |