LNP™ LUBRICOMP™ RFP36 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cFa00W_LNPLUBRICOMPRFP36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated. This product is also known as LUBRICOMP* RFL-4536. Also known as: LNP* LUBRICOMP* Compound RFL-4536 Product reorder name: RFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.97 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.21 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.78 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10500 | MPa | ASTM D638 |
| -- | 9800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 133 | MPa | ASTM D638 |
| Fracture | 135 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.1 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 9400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 195 | MPa | ASTM D790 |
| -- | 207 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.56 | ASTM D3702 Modified | |
| With Self-Static | 0.48 | ASTM D3702 Modified | |
| Wear Factor - Washer | 11.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 780 | J/m | ASTM D4812 |
| 23°C 3 | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 5.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 233 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 236 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4900-611UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| TRIBIT® VS1503 | Samyang Corporation | PBT | TRIBIT® |
| ELASTOSIL® LR 3846/20 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LEXAN™ ML7647K resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Petrothene® NA340212 | LyondellBasell Industries | LDPE | Petrothene® |