DENILUB B 20G 3TF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Vamp Tech |
| Trademark: | DENILUB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cFIETX_DENILUB-B-20G-3TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 30% glass fiber reinforced with PTFE. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.21 | ||
| Static | 0.16 | ||
| Wear Factor 1 | 20.0 | 10^-10 m³ h/N·m·h |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648A |
| Vicat Softening Temperature | 205 | °C | ASTM D1525 2 |
| Note Message | |
|---|---|
| 1 . | Thrust Washer |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beetle® PBTS120S | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| Karina BLACK PVC COMPOUND -E 855-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTP PL001 | Chengdu Letian Plastics Co., Ltd | PPS | LTP |
| Polifor® 7000/V0-AF-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| TECHNYL STAR® S 60G1 V30 GREY R7012 | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |