RALUPOL® UP 8602
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RALUPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cEM2yk_RALUPOL-UP-8602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced Polyester moulding compound Mould shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical strength, good mechanical strength, excellent surface quality and excellent colour stability (non-yellowing), low wear Primary application(s): Oven fittings This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 to 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.90 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.55 | % | ISO 62 |
| Post Shrinkage 2 | < 0.10 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 200 | °C | |
| 20,000 h | 150 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 10000 to 12000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 40.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 14000 to 16000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 90.0 to 120 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 5.0 to 10 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 140 to 170 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 70.0 to 130 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.0E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.50 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 to 1.0E+14 | ohms·cm | IEC 60093 |
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by RASCHIG) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM93-15E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Colorite 12 Series 9612 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| LAMIGAMID® 317 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| PENTAMID L GV30 H natur | PENTAC Polymer GmbH | Nylon 12 | PENTAMID L |
| Sumiliteresin® PR-1019 I | SBHPP | Phenolic | Sumiliteresin® |