SABIC® Vestolen A 5061R 10000
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cCz0Gf_SABIC-Vestolen-A-5061R-10000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® Vestolen A 5061R 10000 (black) is a grade, which has a high density and a bimodal distribution of the molecular mass. An universal grade for pipe extrusion which, due to a keen combination of properties, is typically used for drinking water and waste water piping. This material meets (inter)national standards for use in drinking water and wastewater piping. MRS class ISO 12162 MPa = 8.0 (PE 80). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/5.0 kg | 0.36 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress (Yield, 2.00 mm, Compression Molded) | 23.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Yield, 2.00 mm, Compression Molded) | 9.0 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Compression Molded | 8.6 | kJ/m² | |
| 23°C, Compression Molded | 23 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 42.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 123 to 127 | °C | DIN 53765 |
| Oxidation Induction Time - Compression Molded (210°C) | > 20 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 8.00 | MPa | ISO 12162 |
| RAL Number | 9004 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3890H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SCHULADUR® PCR GF 15 K2027 | A. Schulman Europe | PBT+PET | SCHULADUR® |
| Sylvin 8696-70DB Clear 876 Dry Blend | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Akoalit PB 4267 grey | LyondellBasell Industries | PB | Akoalit |
| Geon™ Vinyl Flexible G92D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |