Ebalta ebatemp / PUR 5
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cCcIwO_Ebalta-ebatemp-PUR-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta ebatemp is a high-quality two-component Polyurethane casting resin, which is very suitable for the production of vacuum thermoformed mouldings. The fast casting resin, which is filled with very fine aluminium powder is very well castable and after curing very well polishable and workable. With ebatemp vacuum thermoformed mouldings can be produced within 1-2 hours, these moldings show a temperature capacity of 80-90°C. Post-curing is not necessary. Material should be carefully stirred up/ shaked before use. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.13 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 77 to 83 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 4300 to 5100 | MPa | ISO 178 |
| Flexural Stress | 35.0 to 45.0 | MPa | ISO 178 |
| Compressive Stress | 51.0 to 61.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.5 to 4.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 87.0 to 93.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 16 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.60 to 1.70 | g/cm³ | |
| Viscosity (25°C) | 1.0 to 1.6 | Pa·s | |
| Curing Time (20°C) | 1.0 to 2.0 | hr | |
| Pot Life 1(20°C) | 4.5 to 5.5 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lumicene® BM 359 SG | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Network Polymers PP PPH 30 1200 TF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| ACCUCOMP™ CP0408L | ACLO Compounders Inc. | PP Copolymer | ACCUCOMP™ |
| Hylon® N1000STH | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| POCAN® B 1600 000000 | LANXESS GmbH | PBT | POCAN® |