RTP 4000 TFE 20
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cBtaN6_RTP-4000-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE Lubricated |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 - 2.5 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 4.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 302 - 329 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1507 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| EVALENE® PP PHJ1202 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| Elvacite® 2043 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| HOPELEN J-150 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| Polyrocks 168(f1) | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |