Hyundai EP PA66 LD910
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cBmvIO_Hyundai-EP-PA66-LD910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Base Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.2 to 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 88.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2940 | MPa | ASTM D790 |
| Flexural Strength | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Melting Temperature | 265 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 3.5 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 21-205 Solution | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Moplen RP210G | LyondellBasell Industries | PP Random Copolymer | Moplen |
| NITRIFLEX N-7920 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Karina COMP. PVC WHITE -E 786-10/332-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| LNP™ STAT-KON™ 9X08403C compound | SABIC Innovative Plastics | TP, Unspecified | LNP™ STAT-KON™ |