Edge™ 8
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Plastic Selection Group, Inc. |
| Trademark: | Edge™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cBOHew_Edge-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edge™ Copolymer is a clear thermoplastic resin that combines crystal clarity and rigidity with superior toughness. Edge™ 8 products were designed to compete with the slightly more brittle resins like GPPS, SAN, or General Purpose Acrylic. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2890 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 63.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 0.125 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 0.50 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 to 188 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 193 to 204 | °C | |
| Nozzle Temperature | 193 to 215 | °C | |
| Processing (Melt) Temp | 204 to 221 | °C | |
| Mold Temperature | 27.0 to 38.0 | °C | |
| Back Pressure | 0.340 to 1.38 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Argothane® ST-1665-90 | Argotec LLC | TPU, Unspecified | Argothane® |
| Gallonprene® GP420-4002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GELAST GT702 | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| Geon™ Vinyl Flexible R343AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LEXAN™ EXL1413T resin | SABIC Innovative Plastics | PC | LEXAN™ |