TECAFORM® TECAFORM®
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cBGy2o_TECAFORM-TECAFORM-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECAFORM® is a semi-crystalline thermoplastic offering high strength, stiffness and toughness. TECAFORM® is resistant to hot water, hydrocarbons and solvents, and it possesses good bearing and wear properties. It is available in natural and black grades. TECAFORM® is commonly used as bushings, rollers, wear strips and other applications requiring a combination of strength, low moisture absorption, chemical resistance and dimensional stability. TECAFORM® is used in a wide variety of industrial applications requiring good strength and toughness, dimensional stability, wear resistance and the ability to operate in a wet environment with little absorption. Material handling, machinery and fluid handling are some of the common industries utilizing TECAFORM®'s combination of properties. Typical applications are gears, wear strips, bushings, pump parts, fittings and rollers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.22 | % | ASTM D570 |
| Saturated, 23°C | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2620 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 75.8 | MPa | ASTM D790 |
| Compressive Strength | 31.0 | MPa | ASTM D695 |
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.21 | ||
| Wear Factor 2(0.28 MPa, 0.25 m/sec) | 130 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| Melting Temperature | 165 | °C | ASTM D2133 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Maximum Service Temperature | |||
| Intermittent | 141 | °C | |
| Long Term 3 | 91 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant 4(23°C, 60 Hz) | 3.70 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Data obtained from extruded shapes |
| Note Message | |
|---|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | Against Steel |
| 3 . | UL 746B |
| 4 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen PP200P | LyondellBasell Industries | PP Random Copolymer | Moplen |
| TRIREX® 3026B(L) | Samyang Corporation | PC | TRIREX® |
| WPP PP PPC4TF1.3-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Gallonprene® GP550-6503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ESPOLEX WT466 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |