PTS PCA-30G11-(V)
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cAfOlt_PTS-PCA-30G11--V-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PTS PCA-30G11-(V) is a polycarbonate + polybutene terephthalate (PC + PBT) product, which contains a 11% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 6.0 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 2860 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 99.0 | °C | ASTM D648 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 98.9 | °C | |
| Drying Time | 4.0 - 12 | hr | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 257 - 279 | °C | |
| Middle Temperature | 246 - 279 | °C | |
| Front Temperature | 246 - 279 | °C | |
| Nozzle Temperature | 246 - 279 | °C | |
| Processing (Melt) Temp | 246 - 279 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Injection Pressure | 110 - 138 | MPa | |
| Back Pressure | 0.689 - 1.38 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.020 - 0.025 | mm |
| Injection instructions |
|---|
| Dew Point, Preferred: -40.0 °CDew point: <-20.0 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP DD2 1x102 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| DENYL P 3010 | Vamp Tech | Nylon+PP | DENYL |
| Expandable PS RF33W-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Sylvin 83029-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8200-80 Clear 8472 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |