LNP™ THERMOCOMP™ EF006 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cATInu_LNP-THERMOCOMP-EF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound EF-1006 Product reorder name: EF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.53 | g/cm³ | ASTM D792 |
| -- | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.49 | % | ISO 294-4 |
| Flow : 24 hr | 0.23 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11400 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 189 | MPa | ASTM D638 |
| Break | 177 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.4 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11400 | MPa | ASTM D790 |
| -- | 11500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 271 | MPa | ASTM D790 |
| -- | 263 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.55 | ||
| vs. Itself - Static | 0.50 | ||
| Wear Factor - Washer | 130 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 760 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.4 | J | ASTM D3763 |
| -- | 2.64 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 206 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 201-87 | ExxonMobil Chemical | TPV | Santoprene™ |
| Braskem PP R131-02A | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Eporex® 500 | Eternal Plastics Co., Ltd. | PS (GPPS) | Eporex® |
| LNP™ STAT-KON™ RE007 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| PENTALLOY BP H natural | PENTAC Polymer GmbH | Nylon 6+PP | PENTALLOY BP |