Pebax® MV 3000 SP 01
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c9gvvb_Pebax-MV-3000-SP-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® MV 3000 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof. This SP grade is specifically designed for outdoor application that needs excellent weather resistance properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 28 | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 35 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 450 | % | ISO 527-2 |
| Flexural Modulus | 45.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission 1 | ASTM E96 | ||
| -- 2 | 19000 to 25000 | g/m²/24 hr | |
| -- 3 | 3100 to 4000 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 158 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 190 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 15 µm, 38°C, 90% RH |
| 2 . | Procedure BW |
| 3 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1320 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Supol HT940UE | LyondellBasell Industries | PP Copolymer | Supol |
| Forprene® 6NM001D50 | SO.F.TER. SPA | TPV | Forprene® |
| KPOL-PP K-PPC 6.0 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |
| POLIMAXX GA400 | IRPC Public Company Limited | ABS | POLIMAXX |