Order Products : sales@su-jiao.com
Leona™ CR103
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c9bKih_Leona-CR103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ CR103 is a Polyamide 66 (Nylon 66) product filled with mineral. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ CR103 include automotive, electrical/electronic applications, engineering/industrial parts and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.45 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.50 to 1.1 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.5 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 94 | 74 | ||
| R-Scale | 120 | 94 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8100 | 5200 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 131 | 100 | MPa | ISO 527-2 |
| -- | 139 | 106 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 6.0 | 9.0 | % | ASTM D638 |
| Break, 23°C | 4.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 6600 | 4200 | MPa | ASTM D790 |
| 23°C | 6700 | 4200 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 213 | 151 | MPa | ASTM D790 |
| 23°C | 203 | 143 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.6 | 5.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | 51 | 59 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® FOR 3390 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Unichem 4875 | Colorite Polymers | PVC, Unspecified | Unichem |
| NAXALOY® 770-NT137 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| Chemraz XCD | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Idemitsu PS NS-321 | Idemitsu PS | PS (HIPS) | Idemitsu PS |