AKROTEK® PK-HM GF 50 natural (4741)
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c83MPu_AKROTEK-PK-HM-GF-50-natural-4741-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PK-HM GF 50 natural (4741) is a 50% glass fibre reinforced Polyketon with very high stiffness and strength and light inherent color. Applications are mainly components in mechanical engineering and the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.65 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 11.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.70 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 0.40 to 0.50 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13900 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 225 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FLEXCHEM™ 5051-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Ecomass® 706BI76 | Ecomass Technologies | ABS | Ecomass® |
| GERMAMID 6 HX | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| LEXAN™ FXE4472L resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Stat-Tech™ PC-10CF/000 FR V0 BLACK | PolyOne Corporation | PC | Stat-Tech™ |