Tenac™-C 3513
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c7aghg_Tenac--C-3513.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C 3513 is an Acetal (POM) Copolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C 3513 include engineering/industrial parts, automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.6 to 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 62.0 | MPa | ISO 527-2 |
| -- | 62.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 35 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2450 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 14.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 158 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 153 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 to 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 to 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Arc Resistance | 250 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-371U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Next Nylon 6 Prime Series NG15-01ABK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| ColorFast® PCT2018 | LTL Color Compounders, Inc. | PC+PBT | ColorFast® |
| Plaslube® PA6/6 GF33 TS15 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Rotuba CAB Reprocessed Grade | Rotuba Extruders, Inc. | CAB | Rotuba CAB |