Latamid SP1
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c6qAmC_Latamid-SP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6.10 (PA6.10). Unfilled. Low moisture absorption. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 to 1.4 | % | |
| Flow : 2.00 mm | 1.0 to 1.4 | % | |
| Water Absorption (23°C, 24 hr) | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2400 | MPa | |
| 60°C | 700 | MPa | |
| 90°C | 450 | MPa | |
| 120°C | 300 | MPa | |
| 150°C | 200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 65.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 100 | % | |
| Break, 60°C | > 100 | % | |
| Break, 90°C | > 100 | % | |
| Break, 120°C | > 100 | % | |
| Break, 150°C | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 175 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 70.0 | °C | |
| Vicat Softening Temperature | 180 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FEA-251U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Sinvicomp SIM5029R | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Huafon HF-1098A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Iupital® FG2025 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| LUVOCOM® 1850/CF/10/GF/10/GK/10/GS/5/FR | Lehmann & Voss & Co. | PBT | LUVOCOM® |