Horda E8472
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c6P33o_Horda-E8472.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
E8472 is a crosslinkable, strippable semiconductive compound, designed for peroxide cured cables with XLPE and EPR insulation and for use in both dry and steam curing processes.E8472 have:
E8472 meets the requirements as below, when optimal processing extrusion and end testing procedure are used:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 27 | MU | ISO 289 |
| Moisture 1 | ppm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2(200°C) | 70 | % | IEC 540 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Stripping Force - EPR 3(23°C) | 1.3 - 1.5 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -10 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | -35 | % | ASTM D573 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 5.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 60.0 | °C | |
| Hopper Temperature | 23.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 100 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 100 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 100 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 100 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 100 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP513 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| SUSTAMID 6G | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Fainplast PVC MPH 57/Y | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ELASTOSIL® R 401/20 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Hifax TRC 277P S81497 | LyondellBasell Industries | PP Copolymer | Hifax |