Generic PBT - Mineral
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c5CYq2_Generic-PBT---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PBT - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 - 1.82 | g/cm³ | ASTM D792 |
| 23°C | 1.41 - 1.81 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.37 - 1.8 | % | ASTM D955 |
| Transverse flow : 23°C | 0.69 - 1.5 | % | ASTM D955 |
| 23°C | 0.69 - 1.8 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.060 - 0.090 | % | ASTM D570 |
| Saturated, 23°C | 0.070 - 0.51 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 - 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 112 - 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2900 - 4260 | MPa | ASTM D638 |
| 23°C | 2800 - 4350 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 48.2 - 58.4 | MPa | ASTM D638 |
| Fracture, 23°C | 46.9 - 56.4 | MPa | ASTM D638 |
| Fracture, 23°C | 45.0 - 60.0 | MPa | ISO 527-2 |
| 23°C | 46.9 - 50.1 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 - 5.4 | % | ASTM D638 |
| Fracture, 23°C | 1.8 - 4.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2930 - 10400 | MPa | ASTM D790 |
| 23°C | 3000 - 4460 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 88.6 - 177 | MPa | ASTM D790 |
| 23°C | 83.1 - 121 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 36 - 47 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 22 - 95 | J/m | ASTM D256 |
| 23°C | 3.0 - 4.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 290 - 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 220 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 120 - 223 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 69.0 - 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 64.8 - 198 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 175 - 216 | °C | ISO 306 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.9E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.8E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 75.0 - 105 | °C | UL 746 |
| RTI Imp | 75.0 - 106 | °C | UL 746 |
| RTI | 75.0 - 106 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 4.0E+14 - 2.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 19 - 25 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 2.90 - 3.80 | ASTM D150 | |
| 23°C | 3.55 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 2.0E-3 - 0.020 | ASTM D150 | |
| 23°C | 1.2E-3 - 0.015 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 140 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.050 | % | |
| Rear Temperature | 230 - 267 | °C | |
| Middle Temperature | 240 - 267 | °C | |
| Front Temperature | 245 - 267 | °C | |
| Nozzle Temperature | 250 - 263 | °C | |
| Processing (Melt) Temp | 250 - 268 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Injection Pressure | 81.4 - 87.9 | MPa | |
| Back Pressure | 0.507 - 0.531 | MPa | |
| Screw Speed | 65 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PBT - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 1200-75A | RTP Company | TPU-Polyester | RTP |
| Fusabond® N493 | DuPont Packaging & Industrial Polymers | Ethylene Copolymer | Fusabond® |
| LOXIM 230 12 V0 | LOXIM Industries Private Limited | PBT | LOXIM |
| TechnoFiber PP LGF 20-10-01 H | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |
| SEQUEL® 1493-UV NH533 | LyondellBasell Industries | PP, Unspecified | SEQUEL® |