Miramid® VE30C

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Leuna GmbH
Trademark:	Miramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	c4wCrD_Miramid-VE30C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Miramid® VE30C is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Europe for injection molding.

Important attributes of Miramid® VE30C are:

Chemical Resistant

Crystalline

Fast Molding Cycle

Good Stiffness

Mold Release Agent

Typical applications include:

Automotive

Engineering/Industrial Parts

Construction Applications

Electrical/Electronic Applications

Housings

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Mold Release
Features	Crystalline Fast Molding Cycle Fuel Resistant Good Flow Good Stability Good Stiffness Grease Resistant High Rigidity Oil Resistant Solvent Resistant
Uses	Automotive Applications Building Materials Electrical/Electronic Applications Engineering Parts Housings Machine/Mechanical Parts Power/Other Tools Sporting Goods
Forms	Granules
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1360	--	kg/m³	ISO 1183 ¹
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)	40.0	--	cm³/10min	ISO 1133
Water Absorption				ISO 62 ²
Saturation	6.3	--	%
Equilibrium	1.7	--	%
Viscosity number	145	--	cm³/g	ISO 307, 1157, 1628 ³

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	9000	6000	MPa	ISO 527-2 ⁴
Tensile Stress (Break)	175	110	MPa	ISO 527-2 ⁵
Tensile Strain (Break)	3.0	6.0	%	ISO 527-2 ⁶
Tensile Creep Modulus (1000 hr)	3200	--	MPa	ISO 899-1
Flexural Stress ⁷	250	150	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁸
-30°C	11.0	--	kJ/m²
23°C	12.0	21.0	kJ/m²
Charpy impact strength				ISO 179/1eU ⁹
-30°C	55.0	--	kJ/m²
23°C	85.0	100	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ¹⁰
0.45 MPa	215	--	°C
1.8 MPa	205	--	°C
Melting Temperature (DSC)	220	--	°C	ISO 3146

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	1.0E+13	1.0E+10	ohms·m	IEC 60093 ¹¹
Dielectric Constant (1 MHz)	3.50	6.00		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.20		IEC 60250 ¹²
Comparative tracking index	550	--		IEC 60112 ¹³

Injection	Dry	Unit
Processing (Melt) Temp	260 to 290	°C
Mold Temperature	80.0 to 120	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Typical values for uncoloured product at 23°C
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
13 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Bakelite® PF 6771	Hexion Inc.	Phenolic	Bakelite®
Clearflex® FF 106	Versalis S.p.A.	LLDPE	Clearflex®
ESENTTIA 06C30DA	Polipropileno del Caribe S.A.	PP Impact Copolymer	ESENTTIA
LUVOCOM® 1-8379	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®
Plaslube® PA6/6 CF10 TS15 BK	Techmer Engineered Solutions	Nylon 66	Plaslube®