PRE-ELEC® TPE 1502
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c39AqK_PRE-ELEC-TPE-1502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® TPE 1502 is a conductive thermoplastic compound based on a thermoplastic elastomer (TPE). Conductivity is achieved by using a special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® TPE 1502 has retained the excellent mechanical properties of the base elastomer. Typical applications include extruded profiles, seals and sheets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.1 | % | ASTM D955 |
| Flow direction | 2.1 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 4.21 | MPa | ASTM D638 |
| 100% strain, 4.00mm | 270 | MPa | ASTM D638 |
| 200% strain, 4.00mm | 360 | MPa | ASTM D638 |
| 300% strain, 4.00mm | 450 | MPa | ASTM D638 |
| 4.00 mm | 4.20 | MPa | ISO 527-2 |
| 100% strain, 4.00mm | 1.90 | MPa | ISO 527-2 |
| 200% strain, 4.00mm | 2.50 | MPa | ISO 527-2 |
| 300% strain, 4.00mm | 3.10 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 650 | % | ASTM D638 |
| Fracture, 4.00mm | 650 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide P1000IX1 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| ISORENE™ AA7C2-7001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| JSR EPR EP57F | JSR Corporation | EPDM | JSR EPR |
| LNP™ STAT-KON™ KX02764 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Infino LM-1090 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |