LONGLITE® PBT 3010-104S
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c2u4OF_LONGLITE-PBT-3010-104S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 3010-104S is a 10% glass fiber reinforced black color injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 to 1.4 | % | |
| Flow | 0.30 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® RP223-60 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Surlyn® 1605 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| Ferro PP TPP20AE33BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Paracril® BJLT M40 | INSA | NBR | Paracril® |
| TOTAL Polyethylene Bio TPSeal® 0750_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |