EPLAMID 6 GFR 30 NC ST
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c2KsgZ_EPLAMID-6-GFR-30-NC-ST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6, reinforced with 30% of glass fiber, heat stabilized, lubricated for injection moulding. Eplamid 6 GFR 30 ST is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.60 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.30 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 30 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 87 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9200 | 8900 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 170 | 150 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 8800 | 8600 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 240 | 220 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 14 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 208 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 215 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | HB | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0201FX | Borealis AG | Plastomer | Queo™ |
| STARLEX E/8025-86 naturale | Daloga srl | TPU-Polyether | STARLEX |
| Wellamid® MR409 22H-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| HANWHA P-1700 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| LNP™ THERMOCOMP™ 5C003 compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |