INNOPOL® PP CS 1-4940 MC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c161w2_INNOPOL-PP-CS-1-4940-MC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-4940 MC is a 40 % mica-filled polypropylene homopolymer compound /PP-H MC40 (ISO 1043)/. This grade is available in nature and custom coloured form as well. Recommended application INNOPOL® CS 1-4940 MC is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.7 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.4 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 4.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 4300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 13 | kJ/m² | ISO 179/1eU |
| 23°C | 23 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 131 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A120 |
| -- | 103 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radel® R-5000 | Solvay Specialty Polymers | PPSU | Radel® |
| TRISTAR® PC-10FR-(V8) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Karina BLACK PVC COMPOUND -E 858-48/ 1-CY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pacrel® 5365N-EA | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Petlon Prime A1-G30-00-NT | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |