Lucon® CP6067
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c0kIQE_Lucon-CP6067.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucon® CP-6067 is a Polycarbonate (PC) material filled with carbon fiber and carbon nano. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lucon® CP-6067 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 60 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 98.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 6280 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.00 to 0.981 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 152 HI | RTP Company | PP Copolymer | RTP |
| Andur 80-5AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Dow Corning® C6-265 | Dow Corning Corporation | Silicone | Dow Corning® |
| Sylvin 3240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ DL002P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |