SOLLAMID A 2700 - A 2730 FV 20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c0RuSD_SOLLAMID-A-2700---A-2730-FV-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID A 2700 - A 2730 FV 20 is a Polyamide 66 (Nylon 66) material filled with 20% glass fiber. It is available in Latin America. Primary attribute of SOLLAMID A 2700 - A 2730 FV 20: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.25 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ASTM D570 |
| Heat Stability | 115 to 120 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 122 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | 5000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 140 | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6000 | 3500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 175 | 110 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Unnotched Izod Impact Strength (23°C) | 9.0 | 14 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | > 200 | -- | °C | |
| 1.8 MPa, Unannealed | > 240 | -- | °C | |
| Melting Temperature | 250 to 260 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2002-4A | Resinoid Engineering Corporation | Phenolic | Resinoid |
| mPact™ D139DK | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| TRANSMARE® 5CGF30 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| APEX® 08-A0349A-83 NT NP | Teknor Apex Company | PVC, Flexible | APEX® |
| Vipel® F701-RTP-13 | AOC, L.L.C. | Polyester Alloy | Vipel® |