OPNYL OP66UT105
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bzMfBI_OPNYL-OP66UT105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.17 mm | 0.80 to 1.1 | % | |
| Across Flow : 3.17 mm | 1.5 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1800 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 25 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1890 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 64.0 | °C | ASTM D648 |
| Peak Melting Temperature | 256 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V859 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ACRYLITE® Film White WF003 | Evonik Cyro LLC | Film, PMMA | ACRYLITE® Film |
| Braskem PP CP 144 | Braskem | PP Copolymer | Braskem PP |
| Diamond ABS 7500E | Network Polymers, Inc. | ABS | Diamond ABS |
| LNP™ THERMOCOMP™ UF006S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |