Tenac™ 2010
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | byDVpf_Tenac-2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ 2010 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ 2010 include automotive, engineering/industrial parts, conveyors and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 94 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 70.0 | MPa | ISO 527-2 |
| -- | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2720 | MPa | ASTM D790 |
| -- | 2700 | MPa | ISO 178 |
| Flexural Strength | 97.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 13.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 163 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Specific Heat | 1470 | J/kg/°C | |
| Thermal Conductivity | 0.23 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 to 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 to 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (23°C, 1 MHz) | 7.0E-3 | ASTM D150 | |
| Arc Resistance | 250 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP CKR448 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Monprene® CP-32060G TR BLK 8131 | Teknor Apex Company | TPE | Monprene® |
| ALTECH® PA66 A 2040/100.01 GF40 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Sylvin 6185-80 White 1379 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 955 resin | SABIC Innovative Plastics | PC | LEXAN™ |