Hostaform® CP15X
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvx7Wx_Hostaform-CP15X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Preliminary Data Sheet Hostaform® acetal copolymer grade CP15X is a creep resistant, high viscosity polymer providing excellent performance in general purpose injection molding. This grade provides overall excellent performance in applications requiring high stiffness over time. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 2.0 | % | ISO 294-4 |
| Flow direction | 2.1 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 66.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 40 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2450 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 167 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 195 - 215 | °C | |
| Processing (Melt) Temp | 200 - 215 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 90.0 - 140 | MPa | |
| Holding Pressure | 90.0 - 140 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 195 to 215°CZone 4 Temperature: 195 to 215°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Metocene MF650Y | LyondellBasell Industries | PP Homopolymer | Metocene |
| Globalene® SH4202 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Polyrocks EP8400X105V-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
| Evoprene™ GC 088 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ GC |
| Sylvin 9658-45UV Brown 7416 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |