LNP™ LUBRICOMP™ RL003 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvvi7r_LNPLUBRICOMPRL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RL003 is a compound based on Nylon 66 resin containing PTFE. Also known as: LNP* LUBRICOMP* Compound RL4030 Product reorder name: RL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 59.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 82.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 60-11 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Sindustris PP M1316 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TOTAL Polystyrene Compound FT876 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Anjacom® R250-GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| elitel UE9200 | UNITIKA Plastics Division | TPC-ET | elitel |