Hostacom HBC 327L NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvuog4_HostacomHBC327LNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom HBC 327L NAT is a 30% talc filled PP homopolymer, with low melt flow rate and good impact resistance. Product is UL listed. Product is available as natural, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 3800 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 2.2 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 18 | kJ/m² | ISO 179/1eU |
| 23°C | 33 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silmar® SIL94BA-1575 | Interplastic Corporation | Polyester, TS | Silmar® |
| apilon 52c® C 60 | API SpA | TPU-Polyester | apilon 52c® |
| DJSilicone NE--D-1/NE-D-1U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Hostalen PP H5416 | LyondellBasell Industries | PP Random Copolymer | Hostalen PP |
| Karina IVORY PVC COMPOUND -E 853-35/ 1-DY-IS(AS-80)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |