Badamid® A70 GF30 TM-Z3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvhBx6_Badamid-A70-GF30-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super impact modified glassfibres reinforced injection moulding grade for technical products with high toughness and stiffness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.9 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8450 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 140 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 3.5 | 5.5 | % | ISO 527-2/5 |
| Flexural Stress 3(23°C) | 185 | 155 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 14 | 17 | kJ/m² | |
| 23°C | 22 | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | 85 | 90 | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² | |
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 16 | 14 | kJ/m² | |
| 23°C | 20 | 24 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 262 | -- | °C | ISO 3146 |
| CLTE 9 | ISO 11359-2 | |||
| Flow : 4.00 mm | 3.1E-5 | -- | cm/cm/°C | |
| Transverse : 4.00 mm | 6.6E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 105 | -- | °C | |
| some hours | 195 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | |||
| -- 10 | -- | 1.0E+10 | ohms | |
| -- | 1.0E+12 | -- | ohms | |
| Volume Resistivity 11 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 12(1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 0.014 | 0.16 | IEC 60250 | |
| Comparative Tracking Index 14 | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 15 | HB | -- | ||
| 1.60 mm 16 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 125x13x0.8 mm |
| 16 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ATC-000/000 AS BLACK | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| Visico™ ME4425/Ambicat™ LE4472 | Borealis AG | XLPE | Visico™ |
| DINAPLEN® PPH1S07 G40 HUV-1013 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| ENPRENE 706 | En Chuan Chemical Industries Co,. Ltd. | SBS | ENPRENE |
| SIBUR Synthetic Rubber DST-30-01V | SIBUR | SBC | SIBUR Synthetic Rubber |