ALTECH® ABS ECO 2017/500 GF17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bufywU_ALTECHABSECO2017500GF17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH®ABS ECO 2017/500 GF17 is an acrylonitrile butadiene styrene (ABS) product, which contains a filler of 17% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 133 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Tensile Stress | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 5400 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 14 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 13 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 3.0 - 8.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 50 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1038 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| SILPURAN® 8630/60 | Wacker Chemie AG | Silicone | SILPURAN® |
| THERMOLAST® K TC4MSB (Series: AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ACLAR® 22A (1.5 mil) | Honeywell | PCTFE | ACLAR® |
| Elastron® G P.G401.A55.N | Elastron USA, Inc. | SEBS | Elastron® G |