PULSE™ 920 MG
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | buWCSX_PULSE-920-MG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An inherently matt medium heat, medium impact PC/ABS resin, PULSE™ 920 MG is designed for interior automotive applications where a matt aesthetic is required. Proprietary low gloss technology allows this unique combination of maximum low gloss aesthetics and physical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1130 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/3.8 kg | 4.0 | g/10 min | |
| 260°C/5.0 kg | 22 | g/10 min | |
| Melt volume-flow rate (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.030 | % | |
| Equilibrium | 0.28 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2050 | MPa | ISO 527-2/1, ISO 527-2 2 4 |
| Tensile Stress | |||
| Yield | 48.0 | MPa | ISO 527-2/50, ISO 527-2 5 |
| Break | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 4.6 | % | ISO 527-2 6 |
| Break | 60 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 7 |
| Flexural Modulus 8 | 2100 | MPa | ISO 178 |
| Flexural Stress 9 | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40°C | 5.0 | kJ/m² | ISO 179 |
| 0°C | 10 | kJ/m² | ISO 179 |
| 23°C | 22 | kJ/m² | ISO 179 |
| -30°C | 30.0 | kJ/m² | ISO 179/1eA 10 |
| 23°C | 45.0 | kJ/m² | ISO 179/1eA 11 |
| Charpy impact strength | ISO 179/1eU 12 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 127 | °C | ISO 75-2/B |
| 0.45 MPa | 126 | °C | ISO 75-2 13 |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| 1.8 MPa | 102 | °C | ISO 75-2 14 |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A120 |
| -- | 122 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 128 | °C | ISO 306 15 |
| CLTE - Flow (0 to 80°C) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 16 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7510 GF 30 FL HY /4 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Ferro PP TPP10AE14NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Fluon® PTFE PB3060 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Forflex® 71G001D62 | SO.F.TER. SPA | TPO (POE) | Forflex® |
| GELOY™ XP7550 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |