Fiberfil® J-60/GB/20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | buF5pe_Fiberfil-J-60-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fiberfil®J-60/GB/20 is a polypropylene homopolymer (PP Homopoly) material containing 20% glass beads. This product is available in North America,. Fiberfil®The main characteristics of J-60/GB/20 are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 - 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (6.35 mm) | 0.90 - 1.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 - 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1550 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 1500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 193 - 210 | °C | |
| Middle Temperature | 204 - 221 | °C | |
| Front Temperature | 199 - 216 | °C | |
| Nozzle Temperature | 204 - 221 | °C | |
| Processing (Melt) Temp | 204 - 227 | °C | |
| Mold Temperature | 26.7 - 54.4 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.172 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 50S5202 | The Matrixx Group, Inc. | PC | Matrixx |
| Witcom PA6 2011/342 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| GAPEX® RPP10EB19AL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina WHITE COLOR CONCENTRATE -E 10/ 77-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 836L | The Plastics Group | Nylon 6 | Polifil® Nylon |