VENYL ZG307 - 7761
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bu7z12_VENYL-ZG307---7761.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL ZG307 - 7761 is a Polyamide 66/6 Copolymer (Nylon 66/6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 to 0.70 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9800 | 5900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | 115 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 3.0 | 6.0 | % | |
| Break | 3.0 | 8.0 | % | |
| Flexural Modulus | 8300 | 4700 | MPa | ISO 178 |
| Flexural Stress | 235 | 140 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 80 | 92 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 242 | -- | °C | ISO 3146 |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | DIN 52328 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 250 to 265 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8200-03 | API Polymers, Inc. | PP Copolymer | Michilene |
| Sylvin 5134-70 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Koylene ADL AM018N | Reliance Industries Limited | PP Homopolymer | Koylene ADL |
| KumhoSunny ABS HGX4400Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Karina BLACK PVC COMPOUND 800-48/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |