LNP™ LUBRICOMP™ DFL22ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | btvOSk_LNP-LUBRICOMP-DFL22ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL22ER is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features of this material include: Wear Resistant, Easy Molding, Mold Release. Also known as: LNP* LUBRICOMP* Compound DFL-4022 EM MR Product reorder name: DFL22ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.33 | g/cm³ | ISO 1183 |
| -- | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.65 | % | ISO 294-4 |
| Flow : 24 hr | 0.50 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4150 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 71.7 | MPa | ASTM D638 |
| Yield | 71.0 | MPa | ISO 527-2 |
| Break | 67.6 | MPa | ASTM D638 |
| Break | 67.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.3 | % | ASTM D638, ISO 527-2 |
| Break | 5.5 | % | ASTM D638 |
| Break | 5.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4140 | MPa | ASTM D790 |
| -- | 3900 | MPa | ISO 178 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.38 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor - Washer | 166 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 23.2 | J | ASTM D3763 |
| -- | 6.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 140 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ V0044G RoHS Natural | PolyOne Corporation | XLPE | Syncure™ |
| Dartek F-101 | DuPont Canada, Inc. - Dartek Division | Nylon 66 | Dartek |
| Epic Urethane RM2007 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Hanwha Total PP HS120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina ORANGE COLOR CONCENTRATE 32/ 60-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |