Borpact™ SH950MO
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borpact™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bteRHk_Borpact-SH950MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SH950MO is a random heterophasic copolymer intended for injection moulding. This grade yields high transparency and deep freeze impact resistance combined with excellent flow properties. The material is nucleated with Borealis Nucleation Technology (BNT). This grade contains antistatic and demoulding additives which, together with enhanced nucleation, create a high potential for cycle time reduction. Products moulded from this grade have an excellent balance of see-through transparency and deep freeze impact resistance. In addition, components have good gloss, very low stress whitening and excellent taste and odour properties. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall- thickness reduction. CAS-No. 9010-79-1 CAS-No. 9002-88-4 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (50.0 mm) | 1050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Flexural Modulus | 950 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 15.0 to 40.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A88BW-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Adiprene® LF 800A | Chemtura | PUR-Ether/TDI | Adiprene® |
| Derakane® 510N | Ashland Performance Materials | Vinyl Ester | Derakane® |
| Gallonprene® GP410-5501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| OmniPro™ HPP LF20 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |