Akulon® S223-HG3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | btPU0Z_AkulonS223HG3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon®S223-HG3 is a polyamide 66 (nylon 66) material, which contains a 15% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. Akulon®The main features of the S223-HG3 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Flow | 1.0 | -- | % | ISO 294-4 |
| Transverse flow | 1.5 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 7.8 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6500 | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 5100 | -- | MPa | ISO 178 |
| Flexural Stress | 175 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.71 mm | HB | -- | IEC 60695-11-10, -20 | |
| 1.6 mm | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 5792N-PE | TSRC Corporation | TPE | T-Blend® |
| Thermoset Plastics SC-113 | Thermoset, Lord Chemical Products | Silicone | Thermoset Plastics |
| Vinnolit® P 80 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| 4POM® 23I10000 | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| K-Resin® SBC KR01 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |