BESTPOLUX PCAHC/02
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | btKfk3_BESTPOLUX-PCAHC-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS black Standard lubrified with heat stabilized. to achieve improvements in injection process and moulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 28 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ISO 527-2 |
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 128 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 2650 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Vi-Chem PVC V212-55 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Enviramid® N1315HL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| OnFlex™ S HF 90A-3S1988 | PolyOne Corporation | TPE | OnFlex™ |
| Durethan® BKV 30 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |