NYCOA Polyamide 1637 W
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bsFvsb_NYCOA-Polyamide-1637-W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 1637 W is a plasticized, heat stabilized extrusion material used by the Wire and Cable Industry for protective jacketing. NYCOA 1637 W has been specifically designed to facilitate ease of processing over a broad range of conditions and to provide outstanding performance in applications involving exposure to elevated temperatures. NYCOA 1637 W meets the rigorous requirements for a protective material and has been recognized by the Underwriters' Laboratories for jacketing of Type THHN and Type THWN thermoplastic-insulated wire. This product is specially formulated to meet the UL requirements for sunlight resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 2.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 73.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2100 | MPa | ASTM D790 |
| Flexural Strength 4 | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 51 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 54.4 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638, 2 in/min: 100+% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL AC-GP2 | Polymer Resources Ltd. | Acetal (POM) Copolymer | PRL |
| Tectron H2398 | TECTRON Systems Pte Ltd | TPV | Tectron |
| SuperLite® SL550900-100 (4.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Karina CLEAR PVC COMPOUND 75/205-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ AT-000/18T-2S BLK | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |