Exelene® HDPE 5502
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Montachem International, Inc. |
| Trademark: | Exelene® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bqsKYG_Exelene-HDPE-5502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Exelene® HDPE 5502: Antioxidant Exelene® HDPE 5502AS: Antioxidant, Antistatic |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.35 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| 60°C, 10% Igepal CO-630, F50 | > 500 | hr | ASTM D1693B |
| 50°C, 3.10 mm, 100% Igepal CO-630, F50 | 45.0 | hr | ASTM D1693A |
| 50°C, 1.90 mm, 100% Igepal CO-630, F50 | 35.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 23°C) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 600 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1380 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 270 | J/m | ASTM D256A |
| Tensile Impact Strength | 242 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Brittleness Temperature 4 | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 5 |
| Melting Temperature | 129 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type I, 13 mm/min |
| 4 . | F50; 25 lbf-in |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-2120A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Nypol® PA A3 HF NTLA010 NR430 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Durethan® BM 240 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |
| JSR EPR EP57P | JSR Corporation | EPDM | JSR EPR |
| MARPOL® COPP 20.4 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |