VALOX™ 357 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bqGBfU_VALOX-357-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced. Applications like bobbins, switches and enclosures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.34 | g/cm³ | ISO 1183 |
| Specific Volume | 0.740 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 9.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.80 to 1.1 | % | |
| Flow 2 | 1.0 to 1.4 | % | |
| Flow : 3.20 mm | 1.0 to 1.4 | % | |
| Across Flow 3 | 0.90 to 1.3 | % | |
| Across Flow 4 | 1.2 to 1.6 | % | |
| Water Absorption | |||
| 24 hr | 0.080 | % | ASTM D570 |
| Saturation, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 5 | 2020 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 6 | 48.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 7 | 42.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 8 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 9 | 54 | % | ASTM D638 |
| Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 10 | 2100 | MPa | ASTM D790 |
| -- 11 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 73.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 12 | 78.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 13 | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 14(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 15 | 10 | kJ/m² | ISO 180/1A |
| 23°C 16 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact (23°C, Total Energy) | 35.8 | J | ASTM D3763 |
| Gardner Impact | ASTM D3029 | ||
| 23°C | 43.4 | J | |
| 23°C 17 | 43.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 98.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 18 | 84.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ASTM D1525 19 |
| -- | 145 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| Ball Pressure Test 20(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 60 to 138°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Air | 19 | kV/mm | |
| 3.20 mm, in Oil | 19 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.20 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.030 | ||
| Arc Resistance 21 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.460 mm | HB | ||
| 0.630 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 750 | °C | |
| 3.00 mm | 725 | °C | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | 5.0 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | Type I, 50 mm/min |
| 8 . | Type I, 50 mm/min |
| 9 . | Type I, 50 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2.0 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 1.3 mm/min |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | Modified |
| 18 . | 80*10*4 mm |
| 19 . | Rate B (120°C/h), Loading 2 (50 N) |
| 20 . | by VDE |
| 21 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F800EPS (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Starpylen HU 70E3 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Sumitomo PP FY3011E | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| UNISOFT TPE™ ST-35A-NT-2-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| CALSIN 110FRF | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |