FRIANYL® XT6 GF45 VOXI
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bpm9I2_FRIANYLXT6GF45VOXI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PPA FLAME RETARDANT COMPOUND
PPA, 45% GLASS FIBER REINFORCED, FLAME RETARDANT V0, PBB AND PBDE FREE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.79 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 23°C | 0.50 | % | ISO 294-4 |
| Flow : 23°C | 0.15 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 15000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 280 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | IEC 60216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.40 mm | V-2 | UL 94 | |
| 0.8 mm | V-0 | UL 94 | |
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.8 mm | 960 | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.8 mm | 850 | °C | IEC 60695-2-13 |
| 3.2 mm | 875 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 20000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5281 Polyol/ 5283 Polyol/ 5281 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| Vi-Chem PVC V141-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Chemlon® 104 H | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Clearblend® 155 | Styrolution | MMBS | Clearblend® |
| Electrafil® PA6/6 CF18 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |